High Cr Wear Plate Cr15Mo3 for Mining Industry Hardness More Than HRC57.4

Product Categories
Wuxi Orient Anti-wear Engineering Co.,Ltd.
Contact Now

High Cr Wear Plate Cr15Mo3 for Mining Industry Hardness More Than HRC57.4

  • 1
  • 2
  • 3

Brand Name : Chen's Liner

Model Number : DF1012

Certification : ISO9001:2008

Place of Origin : Jiangsu,China(Mainland)

MOQ : 2tons

Price : USD 2,000-4,000 per ton

Payment Terms : L/C,T/T

Supply Ability : 25000 Ton/Tons per year.

Delivery Time : It depends on quantity to be ordered.

Packaging Details : Packed by strong steel pallets.

Material : Cr15Mo3

Dimension : As per drawing

Hardness : More than HRC57.4

MOQ : 2 tons

Inspection : UT & MT

Heat Treatment : Quenching and Tempering

Surface quality : Good surface quality after shot blasting

Package : Steel pallet

Contact Now

High Cr Wear Plate Cr15Mo3 for Mining Industry

Hardness More Than HRC57.4

Summarization

High Cr white iron material possess a combination of superior abrasion resistance and a reasonable

degree of toughness. The high Cr castings have longer service life than the other material,such as

high Mn steel and Cr-Mo alloy steel.And now it is widely used in the working condition of high wear and low impact,such as dry grinding process,coal mills,cement mills due to its excellent performance.

Specification

Model Number DF1012
Material High Cr Cast Iron
Hardness ≥HRC57.4
Dimension As per drawing
Process Sand Casting
Impact Value ≥AK 10J
Inspection

Dimensional Inspection

Chemical Composition Inspection

Hardness Inspection

UT Test
Application Coal Mill,Cement Mill,Mining Industry etc.
MOQ 2Tons
Delivery Time Depends on the quantity to be ordered.
Port Shanghai
Package Steel Pallets
Payment Terms T/T,L/C

Product Photo

High Cr Wear Plate Cr15Mo3 for Mining Industry Hardness More Than HRC57.4

High Cr Wear Plate Cr15Mo3 for Mining Industry Hardness More Than HRC57.4

High Cr Wear Plate Cr15Mo3 for Mining Industry Hardness More Than HRC57.4

Technical Parameters

Item High Cr White Iron High Cr Alloy Steel High Mn Steel Ni-hard Cast Iron
C 2.4-3.2 1.1-2.2 0.9-1.3 2.4-3.6
Si 0.6-1.2 0.6-1.2 ≤0.8 ≤0.8
Mn 0.5-1.0 0.5-1.0 11.0-18.0 ≤2.0
Cr 12.0-30.0 11.0-30.0 1.5-2.5 1.5-10
S ≤0.04 ≤0.04 ≤0.04 ≤0.15
P ≤0.06 ≤0.06 ≤0.06 ≤0.15
Mo 0.1-3.0 0.1-3.0 ≤1.0 ≤0.1
Cu 0.1-1.0 0.1-1.0 - -
Ni 0-0.3 0-0.3 - 3.3-10
Re - - - -
Equivalent
Specification		 GB/T8263-1999
AS2027 Cr27
AS2027 CrMo 15/3
AS2027 CrMo 20/2/1
ASTM A532 Class Ⅲ Type A 25%Cr
ASTM A532 Class Ⅱ Type B 15%Cr-Mo
BS 4844 3E
DIN1695
NFA32401		 GB/T5680-1998
DL/T 681-1999
JIS G 5153-1999
ASTM A128
DIN GX120Mn12
AFNORZ120Mn12		 GB/T8263-1999
AS2027/Ni-Cr1-550
AS2027/Ni-Cr2-500
AS2027/Ni-Cr4-500
AS2027/Ni-Cr4-600
AS2027/Ni-Cr4-630
ASTM A532 1-A,B,C,D
ASTM A532 2-A,B,C,D,E
ASTM A532 3-A
Material Type Martensite Matrix Austenitic Mn Steel -
Hardness HRC≥56 HB≤300 HRC≥56
Impact Value AK≥4J AK≥80J -

Process

High Cr Wear Plate Cr15Mo3 for Mining Industry Hardness More Than HRC57.4

Company Introduction

High Cr Wear Plate Cr15Mo3 for Mining Industry Hardness More Than HRC57.4

Inspection Facilities

High Cr Wear Plate Cr15Mo3 for Mining Industry Hardness More Than HRC57.4

High Cr Wear Plate Cr15Mo3 for Mining Industry Hardness More Than HRC57.4


Product Tags:

white metal casting

      

aluminum sand castings

      
Quality High Cr Wear Plate Cr15Mo3 for Mining Industry Hardness More Than HRC57.4 for sale

High Cr Wear Plate Cr15Mo3 for Mining Industry Hardness More Than HRC57.4 Images

Inquiry Cart 0
Send your message to this supplier
 
*From:
*To: Wuxi Orient Anti-wear Engineering Co.,Ltd.
*Subject:
*Message:
Characters Remaining: (0/3000)
 
You May Like